| 廠家(產(chǎn)地) | 美國陶氏 |
|---|---|
| 牌號 | 3004 |
| 加工級別 | 擠出級 |
| 銷售方式 | 品牌經(jīng)銷 |
| 類型 | 標(biāo)準(zhǔn)料 |
| 訂購 | 2 region-detail-feature 已選0千克/0.00元 廠家(產(chǎn)地) |
| "mod mod |
產(chǎn)品細(xì)節(jié)圖
|
| 產(chǎn)品說明 | |
| PRIMACOR™ 3004 is an ethylene acrylic acid copolymer designed for extrusion/coextrusion coating and laminating. It provides excellent hot tack and adhesion to metallic, paper and polyethylene substrates with excellent heat seal strength, even through many oil and powdered products. This resin also offers outstanding resistance to delamination, as well as excellent toughness and environmental stress crack resistance (ESCR). Excellent draw down and edge stabilityExcellent product resistanceExcellent hot tack, heat seal, toughnessHigh performance sealant or tie layer Complies with: U.S. FDA 21 CFR 177.1310(b)EU, No 10/2011Consult the regulations for complete details. | |
| 形式 | 顆粒料 |
| 物理性能 | 額定值 | 單位制 | 測試方法 |
| 比重 | 0.938 | g/cm³ | ASTM D792, ISO 1183 |
| 熔流率 2 (190°C/2.16 kg) | 8.5 | g/10 min | ASTM D1238, ISO 1133 |
| 共聚單體含量 3 | 9.7 | % |
| 機械性能 | 額定值 | 單位制 | 測試方法 |
| 抗張強度 | ASTM D638, ISO 527-2 | ||
| 屈服, 模壓成型 | 7.93 | MPa | |
| 斷裂, 模壓成型 | 17.6 | MPa | |
| 伸長率 (斷裂, 模壓成型) | 600 | % | ASTM D638, ISO 527-2 |
| 熱性能 | 額定值 | 單位制 | 測試方法 |
| 維卡軟化溫度 | 81.1 | °C | ASTM D1525, ISO 306 |
| 溶融溫度（DSC） | 98.0 | °C | Internal Method |
| 擠出 | 額定值 | 單位制 | 測試方法 |
| 熔體溫度 | 260 到 290 | °C | |
| 內(nèi)縮量 (288°C, 25.4 µm) | 50.8 | mm | Internal Method |
| **小涂層厚度 | 10 | µm | Internal Method |
| **小涂層重量 | 9.8 | g/m² | Internal Method |
| 擠壓說明 | |||
| 擠出涂層薄膜的制造條件： 用于處理此樹脂的設(shè)備應(yīng)由耐腐蝕材料制成。建議模具和適配器采用不銹鋼和/或雙面鍍鉻或鍍鎳。 螺桿尺寸：3.5 英寸 (89 mm)；30:1 L/D模具：30 英寸模具切邊至 24 英寸模具間隙：20 密爾 (0.508 mm)熔體溫度：550°F (288°C)輸出：250 磅/小時氣隙：6 英寸 (152 mm) | |||