| 廠家(產地) | 韓國韓華 |
|---|---|
| 牌號 | 2020 |
| 加工級別 | 注塑級 |
| 特性級別 | 透明級,增強級 |
| 用途級別 | 薄膜級 |
| 銷售方式 | 品牌經(jīng)銷 |
| 類型 | 標準料 |
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.926 | g/cc | ||
| 熔體流動速率 | ASTM D-1238 | 0.4 | g/10min | |||
| 機械性能 | 斷裂拉伸強度 | ASTM D-638 | 185 | kg/cm2 | ||
| 斷裂伸長率 | ASTM D-638 | 730 | % | |||
| 斷裂伸長率 | MD | ASTM D-882 | 300 | % | ||
| TD | ASTM D-882 | 630 | % | |||
| 斷裂伸長率 | MD | ASTM D-882 | 300 | % | ||
| TD | ASTM D-882 | 630 | % | |||
| 拉伸斷裂強度 | MD | ASTM D-882 | 270 | kg/cm2 | ||
| TD | ASTM D-882 | 250 | kg/cm2 | |||
| 下降沖擊強度 | ASTM D-1709 | 300 | g | |||
| 熱性能 | 熔點 | ASTM D-1525 | 104 | ℃ | ||
| 維卡軟化點 | ASTM D-1525 | 90 | ℃ | |||
| 其它性能 | 混濁度 | ASTM D-1009 | 6.0 | % | ||
| 醋酸乙烯含量 | HCC Method | 3.5 | Wt% | |||
| 厚度 | HCC | 0.06 | ㎜ | |||
| 拉伸抗熱強度 | MD | ASTM D-1004 | 90 | ASTM D1004 | ||
| TD | ASTM D-1004 | 95 | ASTM D1004 | |||