| 類型 | 標(biāo)準(zhǔn)料 |
| 牌號(hào) | 41H |
| 銷售方式 | 品牌經(jīng)銷 |
| 顏色 | 本色 |
| 用途級(jí)別 | 汽車部件 |
| 品牌 | 美國(guó)首諾 |
| 廠家(產(chǎn)地) | 美國(guó)首諾 |
| 加工級(jí)別 | 注塑級(jí) |
| 特性級(jí)別 | 高抗沖,耐低溫 |
| 規(guī)格級(jí)別 | 熱穩(wěn)定 |
(溫馨提示：因塑料行情每天都會(huì)有變更，頁(yè)面上有些報(bào)價(jià)可能會(huì)與當(dāng)天實(shí)際報(bào)價(jià)有所差異，僅供參考！價(jià)格以當(dāng)天市場(chǎng)行情為準(zhǔn)，歡迎來(lái)電咨詢:18551114352/QQ：357201478)
Vydyne® 41H 聚酰胺66 Ascend Performance Materials Operations LLC 產(chǎn)品說(shuō)明: Vydyne 41H is general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 41H was formulated to provide thermal endurance when used in applications in which continuous or extended high-temperature exposure is anticipated.
Vydyne 41H is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. 單位: 公制 | 英制 Properties 處理 資料 視覺(jué)搜索 曲線數(shù)據(jù) 購(gòu)買地點(diǎn)
| 總體 | |
| 材料狀態(tài) | 已商用：當(dāng)前有效 |
| 資料 1 | Technical Datasheet |
| UL 黃卡 2 | E70062-100757495 |
| 搜索 UL 黃卡 | | Ascend Performance Materials Operations LLC | Vydyne® | | |
| 供貨地區(qū) | |
| 添加劑 | 沖擊改性劑 |
| 特性 | | 沖擊改性 抗溶劑性 抗撞擊性，高 | 可加工性，良好 良好耐磨損性 耐低溫沖擊 | 耐化學(xué)性良好 耐汽油性 耐油性能 | |
| 用途 | | 齒輪 電氣/電子應(yīng)用領(lǐng)域 工業(yè)應(yīng)用 | 緊固件 連接器 汽車領(lǐng)域的應(yīng)用 | 消費(fèi)品應(yīng)用領(lǐng)域 | |
| 機(jī)構(gòu)評(píng)級(jí) | | ASTM D 4066 PA0181 | ASTM D 6779 PA0181 | | |
| 外觀 | 自然色 |
| 形式 | 粒子 |
| 加工方法 | 注射成型 |
| 物理性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測(cè)試方法 |
| 密度 | 1.08 | -- | g/cm3 | ISO 1183 |
| 收縮率 | | | | ISO 294-4 |
| 垂直流動(dòng)方向 : 2.00 mm | 1.6 | -- | % | |
| 流動(dòng)方向 : 2.00 mm | 1.8 | -- | % | |
| 吸水率 | | | | ISO 62 |
| 23°C, 24 hr | 1.0 | -- | % | |
| 平衡, 23°C, 50% RH | 2.1 | -- | % | |
| 機(jī)械性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測(cè)試方法 |
| 拉伸模量 (23°C) | 1860 | 1390 | MPa | ISO 527-2 |
| 拉伸應(yīng)力 | | | | ISO 527-2 |
| 屈服, 23°C | 50.0 | 35.0 | MPa | |
| 斷裂, 23°C | 43.0 | 39.0 | MPa | |
| 拉伸應(yīng)變 (斷裂, 23°C) | 50 | 180 | % | ISO 527-2 |
| 彎曲模量 (23°C) | 1750 | 545 | MPa | ISO 178 |
| 彎曲應(yīng)力 (23°C) | 53.0 | 17.0 | MPa | ISO 178 |
| 沖擊性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測(cè)試方法 |
| 簡(jiǎn)支梁缺口沖擊強(qiáng)度 | | | | ISO 179 |
| -40°C | 20 | 25 | kJ/m2 | |
| -30°C | 35 | 25 | kJ/m2 | |
| 23°C | 76 | 110 | kJ/m2 | |
| 簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 | | | | ISO 179 |
| -30°C | 無(wú)斷裂 | 無(wú)斷裂 | | |
| 23°C | 無(wú)斷裂 | 無(wú)斷裂 | | |
| 懸壁梁缺口沖擊強(qiáng)度 | | | | ISO 180 |
| -40°C | 22 | 25 | kJ/m2 | |
| -30°C | 40 | 29 | kJ/m2 | |
| 23°C | 78 | 88 | kJ/m2 | |
| 熱性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測(cè)試方法 |
| 熱變形溫度 | | | | |
| 0.45 MPa, 未退火 | 145 | -- | °C | ISO 75-2/B |
| 1.8 MPa, 未退火 | 58.0 | -- | °C | ISO 75-2/A |
| 熔融溫度 | 260 | -- | °C | ISO 11357-3 |
| 線形熱膨脹系數(shù) | | | | ISO 11359-2 |
| 流動(dòng) : 23 到 55°C, 2.00 mm | 1.7E-4 | -- | cm/cm/°C | |
| 橫向 : 23 到 55°C, 2.00 mm | 1.5E-4 | -- | cm/cm/°C | |
| RTI Elec | | | | UL 746 |
| 0.750 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | | | | UL 746 |
| 0.750 mm | 75.0 | -- | °C | |
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 75.0 | -- | °C | |
| RTI | | | | UL 746 |
| 0.750 mm | 115 | -- | °C | |
| 1.50 mm | 120 | -- | °C | |
| 3.00 mm | 125 | -- | °C | |
| 電氣性能 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測(cè)試方法 |
| 體積電阻率 (0.750 mm) | 1.0E+10 | -- | ohms·cm | IEC 60093 |
| 介電強(qiáng)度 (1.00 mm) | 14 | -- | kV/mm | IEC 60243 |
| 耐電弧性 (3.00 mm) | PLC 6 | -- | | ASTM D495 |
| 漏電起痕指數(shù) (3.00 mm) | 600 | -- | V | IEC 60112 |
| 高電弧燃燒指數(shù)(HAI) | | | | UL 746 |
| 0.750 mm | PLC 0 | -- | | |
| 1.50 mm | PLC 0 | -- | | |
| 3.00 mm | PLC 0 | -- | | |
| 高電壓電弧起痕速率 (HVTR) | PLC 2 | -- | | UL 746 |
| 熱絲引燃 (HWI) | | | | UL 746 |
| 0.750 mm | PLC 4 | -- | | |
| 1.50 mm | PLC 4 | -- | | |
| 3.00 mm | PLC 3 | -- | | |
| 可燃性 | 干燥 | 調(diào)節(jié)后的 | 單位制 | 測(cè)試方法 |
| UL 阻燃等級(jí) | | | | UL 94 |
| 0.750 mm | HB | -- | | |
| 1.50 mm | HB | -- | | |
| 3.00 mm | HB | -- | | |
| 灼熱絲易燃指數(shù) | | | | IEC 60695-2-12 |
| 0.750 mm | 725 | -- | °C | |
| 1.50 mm | 725 | -- | °C | |
| 3.00 mm | 675 | -- | °C | |
| 熱燈絲點(diǎn)火溫度 | | | | IEC 60695-2-13 |
| 0.750 mm | 750 | -- | °C | |
| 1.50 mm | 750 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| 補(bǔ)充信息 | 干燥 | 調(diào)節(jié)后的 | | 測(cè)試方法 |
| Automotive Materials - (thickness d = 1 mm) | + | -- | | FMVSS 302 |
| 注射 | 干燥 | 單位制 | |
| 干燥溫度 | 80.0 | °C | |
| 干燥時(shí)間 | 4.0 | hr | |
| 建議的最大回制料比例 | 25 | % | |
| 料筒后部溫度 | 280 到 310 | °C | |
| 料筒中部溫度 | 280 到 310 | °C | |
| 料筒前部溫度 | 280 到 310 | °C | |
| 射嘴溫度 | 280 到 310 | °C | |
| 加工（熔體）溫度 | 285 到 305 | °C | |
| 模具溫度 | 65.0 到 95.0 | °C | |