產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 吸水量 | 50%相對濕度 | ASTM D-570 | 0.24 | % |
| 吸水量 | 浸漬平衡點 | ASTM D-570 | 1.00 | % | |
| 吸水量 | 24小時浸漬 | ASTM D-570 | 0.27 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.42 | ||
| 模收縮 | 3.2mm | 1.9-2.2 | % | ||
| 機械性能 | 撓曲系數(shù) | 70℃ | ASTM D-790 | 1515 | MPa |
| 破裂點拉伸變形量 | -55℃ | ASTM D-638 | 15 | % | |
| 撓曲變形強度 | 23℃ | ASTM D-790 | 90 | MPa | |
| 撓曲疲勞忍耐限度 | 50%RH,23℃,106周期 | ASTM D-671 | 28 | MPa | |
| 撓曲系數(shù) | 100℃ | ASTM D-790 | 895 | MPa | |
| 撓曲系數(shù) | 122℃ | ASTM D-790 | 550 | MPa | |
| 拉伸強度 | 23℃ | ASTM D-638 | 66 | MPa | |
| IZOD沖擊試驗 | 23℃ | ASTM D-256 | 75 | j/m | |
| 撓曲系數(shù) | 23℃ | ASTM D-790 | 2940 | MPa | |
| 破裂點拉伸變形量 | 100℃ | ASTM D-638 | >260 | % | |
| 彈性系數(shù) | 23℃ | ASTM D-638 | 3100 | MPa | |
| 拉伸強度 | 70℃ | ASTM D-638 | 46 | MPa | |
| 洛氏硬度 | ASTM D-785 | 120 | R scale | ||
| 壓縮應力 | 23℃,10%變形 | ASTM D-695 | 107 | MPa | |
| 撓曲系數(shù) | -55℃ | ASTM D-790 | 3790 | MPa | |
| 破裂點拉伸變形量 | 23℃ | ASTM D-638 | 50 | % | |
| IZOD沖擊試驗 | 缺口-40℃ | ASTM D-256 | 64 | j/m | |
| 拉伸強度 | 122℃ | ASTM D-638 | 23 | MPa | |
| 抗拉伸沖擊強度 | 長試片23℃ | ASTM D-1822 | 206 | kj/m2 | |
| 拉伸強度 | 100℃ | ASTM D-638 | 30 | MPa | |
| 壓縮應力 | 23℃,1%變形 | ASTM D-695 | 31 | MPa | |
| 負載變形量 | 140kg/cm2,50℃ | ASTM D-621 | 0.7 | % | |
| 破裂點拉伸變形量 | 70℃ | ASTM D-638 | 190 | % | |
| 破裂點拉伸變形量 | 122℃ | ASTM D-638 | >260 | % | |
| 抗剪強度 | 23℃ | ASTM D-732 | 66 | MPa | |
| 洛氏硬度 | ASTM D-785 | 90 | M scale | ||
| 拉伸強度 | -55℃ | ASTM D-638 | 96 | MPa | |
| 電氣性能 | 介電因數(shù) | 50%RH,23℃,106Hz | ASTM D-150 | 0.006 | |
| 容積電阻率 | 23℃,0.2%含水量 | ASTM D-257 | 5×1014 | Ω.cm | |
| 抗電弧 | 3.1mm | ASTM D-495 | 183 | sec | |
| 介電強度 | 瞬間Short time(2.3mm) | ASTM D-149 | 15.8 | kv/mm | |
| 熱性能 | 自燃性 | UL 94 | HB | ||
| 線性熱膨脹系數(shù) | 60～104℃ | ASTM D-696 | 12.2 | 10-5m/m℃ | |
| 介電常數(shù) | 50%RH,23℃,102～106Hz | ASTM D-150 | 3.5 | Ω.cm | |
| 熔點 | ASTM D-2133 | 175 | ℃ | ||
| 熱畸變溫度 | 1.8MPa | ASTM D-648 | 124 | ℃ | |
| 線性熱膨脹系數(shù) | -40～29℃ | ASTM D-696 | 10.4 | 10-5m/m℃ | |
| 平均熱容量上下范圍 | -18～100℃ | 1.47 | KJ/kg℃ | ||
| 熱畸變溫度 | 0.5MPa | ASTM D-648 | 170 | ℃ | |