| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動(dòng)速率 | 200℃,5kg | ASTM D-1238(ISO 1133) | 5.5 | g/10min |
| 熔體流動(dòng)速率 | 200℃,10kg | ASTM D-1238(ISO 1133) | 35 | g/10min | |
| 吸水率 | ASTM D-570 | 0.3 | % | ||
| 物理性能 | 模塑收縮率 | ASTM D-75 | 0.4-0.7 | % | |
| 比重 | ASTM D-792 | 1.04 | |||
| 機(jī)械性能 | 拉伸強(qiáng)度 | 23℃ | ASTM D-638 | 480 | Kg/cm2 |
| 斷裂伸長(zhǎng)率 | ASTM D-638 | 15 | % | ||
| 彎曲強(qiáng)度 | 23℃ | ASTM D-790 | 670 | Kg/cm2 | |
| 彎曲模量 | 23℃ | ASTM D-790 | 24000 | Kg/cm2 | |
| IZOD缺口沖擊強(qiáng)度 | 6.4mm | ASTM D-256 | 22 | kg.cm/cm | |
| 洛氏硬度 | ASTM D-785 | 110 | R scale | ||
| 熱性能 | 熱變形溫度 | 6.4mm,18.6kg/cm2未退火 | ASTM D-648 | 85 | ℃ |
| 阻燃性 | UL-94 | HB | class | ||