| 性能項(xiàng)目 | 試驗(yàn)條件[狀態(tài)] | 測(cè)試方法 | 測(cè)試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 密度 | ASTM D-1505 | 0.919 | g/cm3 | ||
| 熔體流動(dòng)速率 | ASTM D-1238 | 1.0 | g/10min | |||
| 物理性能 | 薄膜厚度 | 25 | μm | |||
| 機(jī)械性能 | 抗張模數(shù) | MD | ASTM D-882 | 2000 | KG/cm2 | |
| TD | ASTM D-882 | 2500 | KG/cm2 | |||
| 撕裂強(qiáng)度 | MD | ASTM D-1004 | 5 | kg/cm | ||
| TD | ASTM D-1004 | 12 | kg/cm | |||
| 拉伸斷裂強(qiáng)度 | MD | ASTM D-882 | 400 | KG/cm2 | ||
| TD | ASTM D-882 | 350 | KG/cm2 | |||
| 尖頭沖擊強(qiáng)度 | ASTM D-1709 | 3.7 | g/μm | |||
| 拉伸屈服強(qiáng)度 | MD | ASTM D-882 | 120 | KG/cm2 | ||
| TD | ASTM D-882 | 110 | KG/cm2 | |||
| 斷裂伸長率 | MD | ASTM D-882 | 650 | % | ||
| TD | ASTM D-882 | 800 | % | |||
| 熱性能 | 維卡軟化點(diǎn) | ASTM D-1525 | 102 | ℃ | ||
| 低溫脆化溫度 | ASTM D-746 | <-70 | ℃ | |||